Asahi-Kasei-Xyron-X9102 (Conditioned)

Asahi-Kasei-Xyron-X9102 (Conditioned) material properties: Density 1.286 g/cm3, Young's modulus 3.03 GPa, Yield strength 76.2 MPa (representative value...

Overview

polymer · engineering polymer grade — Conditioned representative condition

Grade designation: Asahi-Kasei-Xyron-X9102-COND

Asahi-Kasei-Xyron-X9102; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.286 g/cm3
Young's modulus	3.03 GPa
Yield strength	76.2 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.265 W/mK
Heat resistance / melting point	151.6 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.233–1.325; MatWeb: 1.26–1.353; Polymer handbook: 1.223–1.313
Young's modulus (GPa)	CAMPUS Plastics: 2.906–3.083; MatWeb: 3.053–3.242; Polymer handbook: 2.845–3.017
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.255–0.263; MatWeb: 0.285–0.295; Polymer handbook: 0.243–0.25

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Xyron-X9102 (Conditioned)?

The density of Asahi-Kasei-Xyron-X9102 (Conditioned) is 1.286 g/cm3.

What is Asahi-Kasei-Xyron-X9102 (Conditioned) used for?

Asahi-Kasei-Xyron-X9102 (Conditioned) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Xyron-X9102-COND refer to?

Asahi-Kasei-Xyron-X9102-COND refers to the "Conditioned" condition: Conditioned representative condition.

What category of material is Asahi-Kasei-Xyron-X9102 (Conditioned)?

Asahi-Kasei-Xyron-X9102 (Conditioned) is categorized as polymer (family: engineering polymer grade).