Asahi-Kasei-Tenac-LA541 (Conditioned)

Asahi-Kasei-Tenac-LA541 (Conditioned) material properties: Density 1.249 g/cm3, Young's modulus 2.86 GPa, Yield strength 68.4 MPa (representative value...

Overview

polymer · engineering polymer grade — Conditioned representative condition

Grade designation: Asahi-Kasei-Tenac-LA541-COND

Asahi-Kasei-Tenac-LA541; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.249 g/cm3
Young's modulus	2.86 GPa
Yield strength	68.4 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.235 W/mK
Heat resistance / melting point	141.6 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.204–1.361; MatWeb: 1.23–1.321; Polymer handbook: 1.256–1.35
Young's modulus (GPa)	CAMPUS Plastics: 2.742–3.288; MatWeb: 2.889–3.064; Polymer handbook: 3.036–3.223
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.222–0.304; MatWeb: 0.251–0.259; Polymer handbook: 0.281–0.291

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Tenac-LA541 (Conditioned)?

The density of Asahi-Kasei-Tenac-LA541 (Conditioned) is 1.249 g/cm3.

What is Asahi-Kasei-Tenac-LA541 (Conditioned) used for?

Asahi-Kasei-Tenac-LA541 (Conditioned) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Tenac-LA541-COND refer to?

Asahi-Kasei-Tenac-LA541-COND refers to the "Conditioned" condition: Conditioned representative condition.

What category of material is Asahi-Kasei-Tenac-LA541 (Conditioned)?

Asahi-Kasei-Tenac-LA541 (Conditioned) is categorized as polymer (family: engineering polymer grade).