Asahi-Kasei-Leona-B3UGM210 (Conditioned)

Asahi-Kasei-Leona-B3UGM210 (Conditioned) material properties: Density 1.28 g/cm3, Young's modulus 3 GPa, Yield strength 75 MPa (representative value; grade...

Overview

polymer · engineering polymer grade — Conditioned representative condition

Grade designation: Asahi-Kasei-Leona-B3UGM210-COND

Asahi-Kasei-Leona-B3UGM210; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.28 g/cm3
Young's modulus	3 GPa
Yield strength	75 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.26 W/mK
Heat resistance / melting point	150 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.229–1.32; MatWeb: 1.255–1.348; Polymer handbook: 1.218–1.308
Young's modulus (GPa)	CAMPUS Plastics: 2.88–3.054; MatWeb: 3.027–3.214; Polymer handbook: 2.82–2.989
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.25–0.257; MatWeb: 0.279–0.289; Polymer handbook: 0.237–0.244

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Leona-B3UGM210 (Conditioned)?

The density of Asahi-Kasei-Leona-B3UGM210 (Conditioned) is 1.28 g/cm3.

What is Asahi-Kasei-Leona-B3UGM210 (Conditioned) used for?

Asahi-Kasei-Leona-B3UGM210 (Conditioned) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Leona-B3UGM210-COND refer to?

Asahi-Kasei-Leona-B3UGM210-COND refers to the "Conditioned" condition: Conditioned representative condition.

What category of material is Asahi-Kasei-Leona-B3UGM210 (Conditioned)?

Asahi-Kasei-Leona-B3UGM210 (Conditioned) is categorized as polymer (family: engineering polymer grade).