Asahi-Kasei-Leona-A3EG7 (Dry-as-molded)

Asahi-Kasei-Leona-A3EG7 (Dry-as-molded) material properties: Density 1.244 g/cm3, Young's modulus 2.83 GPa, Yield strength 67.2 MPa (representative value...

Overview

polymer · engineering polymer grade — Dry-as-molded representative condition

Grade designation: Asahi-Kasei-Leona-A3EG7-DRY

Asahi-Kasei-Leona-A3EG7; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.244 g/cm3
Young's modulus	2.83 GPa
Yield strength	67.2 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.23 W/mK
Heat resistance / melting point	140 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.2–1.356; MatWeb: 1.226–1.316; Polymer handbook: 1.252–1.345
Young's modulus (GPa)	CAMPUS Plastics: 2.716–3.26; MatWeb: 2.863–3.036; Polymer handbook: 3.01–3.195
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.216–0.299; MatWeb: 0.246–0.253; Polymer handbook: 0.276–0.286

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Leona-A3EG7 (Dry-as-molded)?

The density of Asahi-Kasei-Leona-A3EG7 (Dry-as-molded) is 1.244 g/cm3.

What is Asahi-Kasei-Leona-A3EG7 (Dry-as-molded) used for?

Asahi-Kasei-Leona-A3EG7 (Dry-as-molded) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Leona-A3EG7-DRY refer to?

Asahi-Kasei-Leona-A3EG7-DRY refers to the "Dry-as-molded" condition: Dry-as-molded representative condition.

What category of material is Asahi-Kasei-Leona-A3EG7 (Dry-as-molded)?

Asahi-Kasei-Leona-A3EG7 (Dry-as-molded) is categorized as polymer (family: engineering polymer grade).