Asahi-Kasei-Leona-A3EG6 (Conditioned)

Asahi-Kasei-Leona-A3EG6 (Conditioned) material properties: Density 1.257 g/cm3, Young's modulus 2.89 GPa, Yield strength 70.1 MPa (representative value...

Overview

polymer · engineering polymer grade — Conditioned representative condition

Grade designation: Asahi-Kasei-Leona-A3EG6-COND

Asahi-Kasei-Leona-A3EG6; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.257 g/cm3
Young's modulus	2.89 GPa
Yield strength	70.1 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.241 W/mK
Heat resistance / melting point	143.7 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.21–1.3; MatWeb: 1.236–1.328; Polymer handbook: 1.2–1.356
Young's modulus (GPa)	CAMPUS Plastics: 2.776–2.942; MatWeb: 2.923–3.101; Polymer handbook: 2.716–3.26
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.229–0.234; MatWeb: 0.258–0.267; Polymer handbook: 0.216–0.299

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Leona-A3EG6 (Conditioned)?

The density of Asahi-Kasei-Leona-A3EG6 (Conditioned) is 1.257 g/cm3.

What is Asahi-Kasei-Leona-A3EG6 (Conditioned) used for?

Asahi-Kasei-Leona-A3EG6 (Conditioned) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Leona-A3EG6-COND refer to?

Asahi-Kasei-Leona-A3EG6-COND refers to the "Conditioned" condition: Conditioned representative condition.

What category of material is Asahi-Kasei-Leona-A3EG6 (Conditioned)?

Asahi-Kasei-Leona-A3EG6 (Conditioned) is categorized as polymer (family: engineering polymer grade).