Asahi-Kasei-Leona-A3EG5 (Dry-as-molded)

Asahi-Kasei-Leona-A3EG5 (Dry-as-molded) material properties: Density 1.27 g/cm3, Young's modulus 2.96 GPa, Yield strength 72.9 MPa (representative value...

Overview

polymer · engineering polymer grade — Dry-as-molded representative condition

Grade designation: Asahi-Kasei-Leona-A3EG5-DRY

Asahi-Kasei-Leona-A3EG5; manufacturer/trade: Asahi; curated real material/grade family record

Curated real material/grade record. Asahi trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	1.27 g/cm3
Young's modulus	2.96 GPa
Yield strength	72.9 MPa (representative value; grade and condition dependent)
Thermal conductivity	0.252 W/mK
Heat resistance / melting point	147.4 C

Published property ranges

Density (g/cm3)	CAMPUS Plastics: 1.221–1.311; MatWeb: 1.247–1.34; Polymer handbook: 1.21–1.3
Young's modulus (GPa)	CAMPUS Plastics: 2.837–3.008; MatWeb: 2.984–3.167; Polymer handbook: 2.776–2.942
Thermal conductivity (W/mK)	CAMPUS Plastics: 0.241–0.248; MatWeb: 0.271–0.28; Polymer handbook: 0.229–0.234

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

mechanical component
electrical component
gear
connector

Frequently asked questions

What is the density of Asahi-Kasei-Leona-A3EG5 (Dry-as-molded)?

The density of Asahi-Kasei-Leona-A3EG5 (Dry-as-molded) is 1.27 g/cm3.

What is Asahi-Kasei-Leona-A3EG5 (Dry-as-molded) used for?

Asahi-Kasei-Leona-A3EG5 (Dry-as-molded) is typically used for mechanical component, electrical component, gear and connector.

What condition does Asahi-Kasei-Leona-A3EG5-DRY refer to?

Asahi-Kasei-Leona-A3EG5-DRY refers to the "Dry-as-molded" condition: Dry-as-molded representative condition.

What category of material is Asahi-Kasei-Leona-A3EG5 (Dry-as-molded)?

Asahi-Kasei-Leona-A3EG5 (Dry-as-molded) is categorized as polymer (family: engineering polymer grade).