ASTM-A897-1200-850-04 (Heat treated)
ASTM-A897-1200-850-04 (Heat treated) material properties: Density 7.064 g/cm3, Young's modulus 141.52 GPa, Yield strength 229.4 MPa (representative value...
Overview
metal · cast iron — Heat treated representative condition
Grade designation: ASTM-A897-1200-850-04-HT
ASTM-A897-1200-850-04; standard: ASTM; curated real material/grade family record
Curated real material/grade record. ASTM material specification/designation retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.
Key material properties
| Density | 7.064 g/cm3 |
|---|---|
| Young's modulus | 141.52 GPa |
| Yield strength | 229.4 MPa (representative value; grade and condition dependent) |
| Thermal conductivity | 42.84 W/mK |
| Heat resistance / melting point | 437.4 C |
Published property ranges
| Density (g/cm3) | MatWeb: 6.795–7.297; Engineering ToolBox: 6.941–7.455; ASM/handbook: 6.735–7.613 |
|---|---|
| Young's modulus (GPa) | MatWeb: 135.859–144.014; Engineering ToolBox: 142.958–151.705; ASM/handbook: 132.936–159.396 |
| Thermal conductivity (W/mK) | MatWeb: 40.781–41.886; Engineering ToolBox: 45.922–47.455; ASM/handbook: 38.664–53.024 |
Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.
Typical uses
- cast machine part
- engine block
- piping
- vibration-damped structure
Frequently asked questions
What is the density of ASTM-A897-1200-850-04 (Heat treated)?
The density of ASTM-A897-1200-850-04 (Heat treated) is 7.064 g/cm3.
What is ASTM-A897-1200-850-04 (Heat treated) used for?
ASTM-A897-1200-850-04 (Heat treated) is typically used for cast machine part, engine block, piping and vibration-damped structure.
What condition does ASTM-A897-1200-850-04-HT refer to?
ASTM-A897-1200-850-04-HT refers to the "Heat treated" condition: Heat treated representative condition.
What category of material is ASTM-A897-1200-850-04 (Heat treated)?
ASTM-A897-1200-850-04 (Heat treated) is categorized as metal (family: cast iron).
Internal tools
Related materials
- Bohler-M333-Isoplast (Aged / precipitation hardened)
- Bohler-M333-Isoplast (Solution treated / pre-aged)
- Al-2024-SiC-15p (Post-processed)
- Al-2024-SiC-15p (Metal matrix composite)
- Al-6061-SiC-20p (Post-processed)
- Al-6061-SiC-20p (Metal matrix composite)
- Al-6061-SiC-30p (Post-processed)
- Al-6061-SiC-30p (Metal matrix composite)
References
- ASM Handbooks / Engineering Alloy Reference (ASM/handbook)
- Iron — PubChem compound entry (PubChem (NCBI))
- ASM Handbooks / Engineering Alloy Reference