Alumina-TiC-cutting (High-temperature service)
Alumina-TiC-cutting (High-temperature service) material properties: Density 2.62 g/cm3, Young's modulus 223.3 GPa, Yield strength 359.6 MPa (representative...
Overview
ceramic · ceramic matrix composite — High-temperature service representative condition
Grade designation: Alumina-TiC-cutting-HT
Alumina-TiC-cutting; manufacturer/trade: Alumina; curated real material/grade family record
Curated real material/grade record. Alumina trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.
Key material properties
| Density | 2.62 g/cm3 |
|---|---|
| Young's modulus | 223.3 GPa |
| Yield strength | 359.6 MPa (representative value; grade and condition dependent) |
| Thermal conductivity | 18.54 W/mK |
| Heat resistance / melting point | 1322.7 C |
Published property ranges
| Density (g/cm3) | MatWeb: 2.512–2.697; AZoM: 2.437–2.755; ASM/handbook: 2.49–2.674 |
|---|---|
| Young's modulus (GPa) | MatWeb: 214.368–227.427; AZoM: 199.162–239.096; ASM/handbook: 209.933–222.622 |
| Thermal conductivity (W/mK) | MatWeb: 17.885–18.458; AZoM: 14.982–20.686; ASM/handbook: 17.038–17.541 |
Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.
Typical uses
- turbine component
- brake
- thermal protection
- fusion material
Frequently asked questions
What is the density of Alumina-TiC-cutting (High-temperature service)?
The density of Alumina-TiC-cutting (High-temperature service) is 2.62 g/cm3.
What is Alumina-TiC-cutting (High-temperature service) used for?
Alumina-TiC-cutting (High-temperature service) is typically used for turbine component, brake, thermal protection and fusion material.
What condition does Alumina-TiC-cutting-HT refer to?
Alumina-TiC-cutting-HT refers to the "High-temperature service" condition: High-temperature service representative condition.
What category of material is Alumina-TiC-cutting (High-temperature service)?
Alumina-TiC-cutting (High-temperature service) is categorized as ceramic (family: ceramic matrix composite).
Internal tools
Related materials
- BN-Si3N4-composite (Ceramic matrix composite)
- BN-Si3N4-composite (High-temperature service)
- Hexcel-HexPly-APC-2-PEEK-AS4 (Laminate)
- Hexcel-HexPly-APC-2-PEEK-AS4 (Molded composite)
- Hexcel-HexPly-APC-2-PEEK (Laminate)
- Hexcel-HexPly-APC-2-PEEK (Molded composite)
- Hexcel-HexPly-CF-PEEK (Laminate)
- Hexcel-HexPly-CF-PEEK (Molded composite)
References
- ASM Handbooks / Engineering Alloy Reference (ASM/handbook)
- Aluminum oxide — PubChem compound entry (PubChem (NCBI))
- ASM Handbooks / Engineering Alloy Reference