Alumina-TiC-composite (High-temperature service)

Alumina-TiC-composite (High-temperature service) material properties: Density 2.616 g/cm3, Young's modulus 222.64 GPa, Yield strength 357.7 MPa...

Overview

ceramic · ceramic matrix composite — High-temperature service representative condition

Grade designation: Alumina-TiC-composite-HT

Alumina-TiC-composite; manufacturer/trade: Alumina; curated real material/grade family record

Curated real material/grade record. Alumina trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.

Key material properties

Density	2.616 g/cm3
Young's modulus	222.64 GPa
Yield strength	357.7 MPa (representative value; grade and condition dependent)
Thermal conductivity	18.432 W/mK
Heat resistance / melting point	1318.2 C

Published property ranges

Density (g/cm3)	MatWeb: 2.508–2.694; AZoM: 2.434–2.751; ASM/handbook: 2.487–2.67
Young's modulus (GPa)	MatWeb: 213.734–226.741; AZoM: 198.528–238.41; ASM/handbook: 209.299–221.936
Thermal conductivity (W/mK)	MatWeb: 17.764–18.327; AZoM: 14.861–20.555; ASM/handbook: 16.917–17.41

Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.

Typical uses

turbine component
brake
thermal protection
fusion material

Frequently asked questions

What is the density of Alumina-TiC-composite (High-temperature service)?

The density of Alumina-TiC-composite (High-temperature service) is 2.616 g/cm3.

What is Alumina-TiC-composite (High-temperature service) used for?

Alumina-TiC-composite (High-temperature service) is typically used for turbine component, brake, thermal protection and fusion material.

What condition does Alumina-TiC-composite-HT refer to?

Alumina-TiC-composite-HT refers to the "High-temperature service" condition: High-temperature service representative condition.

What category of material is Alumina-TiC-composite (High-temperature service)?

Alumina-TiC-composite (High-temperature service) is categorized as ceramic (family: ceramic matrix composite).