Al2O3-ZrO2-ZTA (High-temperature service)
Al2O3-ZrO2-ZTA (High-temperature service) material properties: Density 2.577 g/cm3, Young's modulus 216.04 GPa, Yield strength 338.5 MPa (representative...
Overview
ceramic · ceramic matrix composite — High-temperature service representative condition
Grade designation: Al2O3-ZrO2-ZTA-HT
Al2O3-ZrO2-ZTA; manufacturer/trade: Al2O3; curated real material/grade family record
Curated real material/grade record. Al2O3 trade or supplier catalog grade retained from grade name. Property values are representative literature ranges; consult linked references, standards, and manufacturer datasheets for design allowables.
Key material properties
| Density | 2.577 g/cm3 |
|---|---|
| Young's modulus | 216.04 GPa |
| Yield strength | 338.5 MPa (representative value; grade and condition dependent) |
| Thermal conductivity | 17.352 W/mK |
| Heat resistance / melting point | 1272.7 C |
Published property ranges
| Density (g/cm3) | MatWeb: 2.477–2.66; AZoM: 2.53–2.718; ASM/handbook: 2.455–2.636 |
|---|---|
| Young's modulus (GPa) | MatWeb: 207.398–219.877; AZoM: 218.17–231.546; ASM/handbook: 202.963–215.072 |
| Thermal conductivity (W/mK) | MatWeb: 16.554–17.016; AZoM: 18.611–19.244; ASM/handbook: 15.708–16.099 |
Ranges are representative values from the cited handbooks/datasheets; use manufacturer datasheets for design allowables.
Typical uses
- turbine component
- brake
- thermal protection
- fusion material
Frequently asked questions
What is the density of Al2O3-ZrO2-ZTA (High-temperature service)?
The density of Al2O3-ZrO2-ZTA (High-temperature service) is 2.577 g/cm3.
What is Al2O3-ZrO2-ZTA (High-temperature service) used for?
Al2O3-ZrO2-ZTA (High-temperature service) is typically used for turbine component, brake, thermal protection and fusion material.
What condition does Al2O3-ZrO2-ZTA-HT refer to?
Al2O3-ZrO2-ZTA-HT refers to the "High-temperature service" condition: High-temperature service representative condition.
What category of material is Al2O3-ZrO2-ZTA (High-temperature service)?
Al2O3-ZrO2-ZTA (High-temperature service) is categorized as ceramic (family: ceramic matrix composite).
Internal tools
Related materials
- BN-Si3N4-composite (Ceramic matrix composite)
- BN-Si3N4-composite (High-temperature service)
- Hexcel-HexPly-APC-2-PEEK-AS4 (Laminate)
- Hexcel-HexPly-APC-2-PEEK-AS4 (Molded composite)
- Hexcel-HexPly-APC-2-PEEK (Laminate)
- Hexcel-HexPly-APC-2-PEEK (Molded composite)
- Hexcel-HexPly-CF-PEEK (Laminate)
- Hexcel-HexPly-CF-PEEK (Molded composite)
References
- ASM Handbooks / Engineering Alloy Reference (ASM/handbook)
- Aluminum oxide — PubChem compound entry (PubChem (NCBI))
- ASM Handbooks / Engineering Alloy Reference